如果彩涂鋁板加工后的顏色的實(shí)際效果不能超過(guò)估計(jì)的實(shí)際效果，將對(duì)其應(yīng)用造成相當(dāng)大的危害。在制造中，影響彩涂鋁板加工表面的色差有哪些?鋁板加工廠家為您講解。
If the actual effect of the color of the color coated aluminum plate after processing cannot exceed the estimated actual effect, it will cause considerable harm to its application. In manufacturing, what are the color differences that affect the processing surface of color-coated aluminum plate? The aluminum plate processing factory will explain to you.
1.染色水溶液溫度。
1. Dyeing water solution temperature.
鋁板的染色分為冷染色和熱染色。冷染在加工過(guò)程中使用時(shí)間較長(zhǎng)，所以對(duì)色彩對(duì)稱性的把握很好。熱染色的使用時(shí)間較短，但沒有辦法控制顏色。熱染色溫度一般為40℃和60℃。如果溫度過(guò)高，則會(huì)降低染色的吸收率，很容易使鋁板表面充分綻放。
The dyeing of aluminum plate is divided into cold dyeing and hot dyeing. Cold dyeing is used for a long time in the processing process, so the color symmetry is well grasped. The use time of thermal dyeing is short, but there is no way to control the color. The thermal dyeing temperature is generally 40 ℃ and 60 ℃. If the temperature is too high, the absorption rate of dyeing will be reduced, and it is easy to make the surface of aluminum plate fully bloom.
2.空氣氧化膜對(duì)鋁單板質(zhì)量的危害。
2. The harm of air oxide film to the quality of aluminum veneer.
空氣氧化膜是指鋁單板的厚度、孔隙率和透明度。鋁板內(nèi)空氣氧化膜的厚度可維持在10μm左右，從而獲得孔隙率和透明度，獲得較好的染色質(zhì)量。
Air oxide film refers to the thickness, porosity and transparency of aluminum veneer. The thickness of air oxide film in aluminum plate can be maintained at 10 μ M to obtain porosity and transparency and better dyeing quality.

3.染色溶液濃度。
3. Dyeing solution concentration.
染色劑的濃度與染色劑有關(guān)。鋁單板上色后，濃度較低，輕濃度稍高。如果濃度過(guò)高，會(huì)造成顏色不均勻或上下波動(dòng)，這在清洗和關(guān)閉“流體顏色”的整個(gè)過(guò)程中很容易發(fā)生。為了提高染料對(duì)染料的吸收能力，選擇低濃度的顏色增加染色，使染料分子結(jié)構(gòu)更均勻地進(jìn)入空氣氧化膜孔中，使顏色更協(xié)調(diào)強(qiáng)。
The concentration of dye is related to the dye. After the aluminum veneer is colored, the concentration is lower, and the light concentration is slightly higher. If the concentration is too high, it will cause uneven color or fluctuation, which is easy to occur during the whole process of cleaning and closing the "fluid color". In order to improve the absorption capacity of the dye to the dye, select the color with low concentration to increase the dyeing, so that the molecular structure of the dye can enter the air oxide film hole more evenly, and make the color more harmonious and strong.
4.鋁型材雙板零件原材料的危害。
4. Hazards of raw materials of aluminum profile double-plate parts.
正常情況下，高純鋁、鋁鎂、鋁錳鋁合金在氧化處理過(guò)程中，其染色特性好，可染成多種顏色。對(duì)于硅或銅重板，在整個(gè)染色過(guò)程中只有深褐色和灰黑色，顏色比較簡(jiǎn)單。
Under normal conditions, high-purity aluminum, aluminum-magnesium, aluminum-manganese aluminum alloys have good dyeing characteristics and can be dyed into various colors during oxidation treatment. For silicon or copper heavy plates, there are only dark brown and gray black in the whole dyeing process, and the color is relatively simple.
哪些原因會(huì)影響到彩涂鋁板加工的色差？我們從四個(gè)方面來(lái)講解了這個(gè)問(wèn)題，您有何疑惑或者需求可以隨時(shí)來(lái)我們網(wǎng)站http://www.ssstlc.com咨詢！
What causes will affect the color difference of color coated aluminum plate processing? We have explained this problem from four aspects. If you have any doubts or needs, please come to our website at any time http://www.ssstlc.com consulting service