鋁卷在成卷之前，需要做一些預(yù)處理工作，以保證鋁卷表面的清潔，以免其表面存在殘留的油脂及潤(rùn)滑劑，對(duì)涂裝及使用產(chǎn)生影響。下面鋁卷加工廠家為您解答相關(guān)：
Before the aluminum coil is rolled, some pretreatment work needs to be done to ensure the cleanness of the surface of the aluminum coil, so as to prevent the residual grease and lubricant on the surface from affecting the coating and use. The following aluminum coil processing factory will answer your questions:
一、可以使用熱水對(duì)鋁卷進(jìn)行清洗。熱水清洗主要是將基板表面殘留的脫脂劑清洗干凈，保證這些殘留物能溶解其中，以防這些脫脂劑對(duì)基板造成二次污染。使用方式多為浸洗和噴淋刷洗的方式。所用水質(zhì)硬度不要太高，否則，水中的礦物質(zhì)會(huì)在基板表面生成礦斑。
1、 The aluminum coil can be cleaned with hot water. Hot water cleaning is mainly to clean the residual degreasing agent on the surface of the substrate to ensure that these residues can be dissolved, so as to prevent these degreasing agents from causing secondary pollution to the substrate. The use methods are mainly immersion and spray brushing. The hardness of the water used should not be too high, otherwise, minerals in the water will form mineral spots on the surface of the substrate.
二、熱堿脫脂由于預(yù)涂線線速較快，所以所用的脫脂劑一般濃度較高，典型的脫脂劑含有氫氧化鈉(NaOH)、碳酸鈉(Na2Co3)、水玻璃(Na2SiO3)、磷酸鹽等組份。熱堿脫脂工序一般分兩步處理以確保鋁卷基板表面清洗干凈，且多用噴淋刷洗的方式。
2、 Due to the fast linear speed of the precoating line, the degreasing agent used is generally of high concentration. Typical degreasing agents include sodium hydroxide (NaOH), sodium carbonate (Na2Co3), sodium silicate (Na2SiO3), phosphate and other components. The hot alkali degreasing process is generally divided into two steps to ensure that the surface of the aluminum coil substrate is cleaned, and spray brushing is often used.

三、對(duì)鋁卷進(jìn)行鈍化處理。鈍化處理是通過(guò)加壓噴淋、浸涂或輥涂等方式使鈍化劑在基材表面形成轉(zhuǎn)化膜。一般使用加壓噴淋的方式，鈍化液在使用過(guò)程中產(chǎn)生的泥渣往往會(huì)堵塞噴孔，從而影響噴淋得效果。浸涂的方式雖然解決了這一問(wèn)題，但鈍化液的消耗量較大。
3、 The aluminum coil shall be passivated. Passivation treatment is to make the passivator form a conversion film on the substrate surface by pressure spraying, dip coating or roller coating. Generally, pressurized spray is used. The sludge produced by the passivation liquid in the process of use often blocks the spray hole, thus affecting the spray effect. Although the dip-coating method solves this problem, the consumption of passivation solution is large.
以上兩種方法在實(shí)際操作中都需要用水沖洗多余的鈍化液，就會(huì)產(chǎn)生廢水的回收和凈化問(wèn)題，輥涂是好的鈍化施工方式，具有涂布均勻、經(jīng)濟(jì)實(shí)用、不需淋洗等優(yōu)點(diǎn)。
The above two methods need to wash the excess passivation solution with water in actual operation, which will cause the problem of wastewater recovery and purification. Roller coating is a good passivation construction method, with the advantages of uniform coating, economic and practical, and no need for rinsing.
鋁卷一般采用鉻酸鹽/氧化物型處理劑，該類處理劑含有鉻酸鹽、鉻酸、磷酸及促進(jìn)劑氟化物和鉬酸鹽。該類處理劑須加入磷酸，否則就不能用來(lái)處理食品和飲料用鋁卷。更多相關(guān)事項(xiàng)就來(lái)我們網(wǎng)站http://www.ssstlc.com咨詢吧！
Generally, chromate/oxide type treatment agent is used for aluminum coil, which contains chromate, chromic acid, phosphoric acid and accelerator fluoride and molybdate. This kind of treatment agent must be added with phosphoric acid, otherwise it cannot be used to treat aluminum rolls for food and drink. Come to our website for more relevant matters http://www.ssstlc.com Ask!